ZZ® 330 Fire Protection Foam Starter-Kit
In addition to its outstanding technical fire safety properties, ZZ® 330 Fire Protection Foam is particularly characterised by its easy processing. It can be used as a mixed penetration seal (EI 90), as well as a pure cable penetration seal (EI 60/ EI 90/ EI 120). The optimal match between the beginning of the reaction and hardening enables sufficiently long work interruptions for the user, as well as fast work progress. Thanks to the high viscosity, the user does not have to deal with foam running out of the penetration seal. After hardening, the permanently elastic structure of the penetration seal enables easy retroactive-installation.
| Name | ZZ® 330 Fire Protection Foam Starter-Kit |
| Manufacturer | ZAPP-ZIMMERMANN |
| Designation | Art. no. | PU | |
|---|---|---|---|
| ZZ® 330 Fire Protection Foam Starter-Kit | B16N00-0315 | 1 | |
Detailed information
- Downloads
- Description
- Trade name: ZZ® 330 Fire Protection Foam Starter-Kit
- Additional Information
Product Information 1 x 380 ml cartridge, 1 x Cartridge Gun EasyMax 2K, incl. accessories
Compression hardness Cv (40%) = 18kPa Test standard: DIN EN ISO 3386-1 Classification of the reaction to fire according to DIN EN 13501-1 Class E Building material class DIN 4102-B2 Thermal stress Continuous contact or ambient temperature: ≤ 80 °C Indoor air hygiene Requirements according to AgBB scheme 2015 are met Test standards: prEN 16516, ISO 16000-3, ISO 16000-6, ISO 16000-9 Surface resistivity R0 = 2 x 109 Ω Test standard: BGR 132:2003 (2.6), DIN IEC 60167 (For requests for installation in hazardous areas please contact ZAPP-ZIMMERMANN GmbH) airborne sound insulation Dn,e,w(C;Ctr) = 66 (-1; -7) dB Rw(C;Ctr) = 47 (-1; -7) dB Test standard: EN ISO 717-1 (Specimen dimensions 350 x 350 x 170 [mm], tested without installations) Thermal conductivity λ = 0,088 W/(m*K); R = 0,279 m²*K/W; Test standard: DIN EN 12667 Resistance to static differential pressure Pmax = 8800 Pa Test standard: Based on EN 12211 (Specimen dimensions 360 x 360 x 144 [mm], tested without installations) Expansion ratio 1.6 to 4.5 times. Tested on samples at 450 °C for 25 minutes with applied load. The expansion factor is a laboratory parameter. The expansion behavior in the installed state depends on the existing boundary conditions. Expansion pressure No expansion pressure measurable Bulk density ρ ≥ 215 kg/ Cutability After approx. 90 seconds (at 72 °F /22 °C material temperature and ambient temperature) Work interruption approx. 50 seconds (at 22 °C material temperature and ambient temperature) The specifications vary depending on the material and ambient temperature. Foam yield Up to 2.1 litres (at 22 °C material temperature and ambient temperature) Application temperature 59 °F to 86 °F (15 °C to 30 °C), recommended: 68 °F – 77 °F (20 °C to 25 °C) Transport / storage dry in original containers Storage temperature 5 °C – 30 °C